NON LATEX DENTAL DAM

by
by
NON LATEX DENTAL DAM 2
Type
  • Polyisoprene Dental Dam, Powder-Free, Smooth, Non-sterile
Material
  • 100% Synthetic Polyisoprene Quality Latex
Colours
  • Purple
Scent
  • Vanilla
Design & Features
  • High quality, polyisoprene rubber, strong and tear resistance, for single use only
Storage Condition
  • Non-latex dental dam shall maintain their properties when stored in a cool and dry place. Avoid direct sunlight
Shelf-life
  • 3 years from the date of manufacture with the above storage condition
Packing Style
  • “6 x 6”: 36 pieces/box, 40 boxes per carton

 

SEND INQUIRY

FUNCTIONAL BENEFITS:

  • Reduce risk of latex allergic reactions
  • Protect the treated area from being exposed to oral bacteria
  • Prevent the patient’s tongue and gums from irritation during treatment
  • Prevent any debris from falling to the patient’s throat
  • Better colour contrast to enhance tooth visibility

QUALITY STANDARDS:

  • Manufactured in accordance to ISO 9001:2015 and ISO 13485:2016
Regular Quadrilateral Dimension (mm) Thickness (mm) Specification
152mm x 152mm
(6 inch x 6 inch)		 0.18 + 0.02 (Medium)
Property In-House Specification
Before Aging After Aging
(166 hours @ 70°C)
Elongation at Break (%) Min 700 Min 600
Tensile Strength (MPa) Min 20 Min 17

*Remark: Tested according to In-House Standard using dumbbell cutter which comply to ASTM D412 test method

FUNCTIONAL BENEFITS

FUNCTIONAL BENEFITS:

  • Reduce risk of latex allergic reactions
  • Protect the treated area from being exposed to oral bacteria
  • Prevent the patient’s tongue and gums from irritation during treatment
  • Prevent any debris from falling to the patient’s throat
  • Better colour contrast to enhance tooth visibility

QUALITY STANDARDS:

  • Manufactured in accordance to ISO 9001:2015 and ISO 13485:2016
PHYSICAL DIMENSION
Regular Quadrilateral Dimension (mm) Thickness (mm) Specification
152mm x 152mm
(6 inch x 6 inch)		 0.18 + 0.02 (Medium)
PHYSICAL PROPERTIES
Property In-House Specification
Before Aging After Aging
(166 hours @ 70°C)
Elongation at Break (%) Min 700 Min 600
Tensile Strength (MPa) Min 20 Min 17

*Remark: Tested according to In-House Standard using dumbbell cutter which comply to ASTM D412 test method